Folks, Readers may remember that I have had an interest in tin pest for some time. Tin pest can occur if nearly pure tin is exposed to cold temperatur...
Tin Silver
Solder Technology Inside A Hot Car On A Sunny Summer Day
Here’s a true story regarding the service temperature of solder joints. Yesterday, as I left work, I noticed that it felt really hot outside. I ...
Specifying Solder Preforms - The Perfect Alloy
I’ve always been a strong believer that a customer should not get a solder alloy that just “works” for their application, they shoul...
Low Temperature Solders Slated to Leave Niche Status by 2017
Folks, It surprises many people that the foundation metal of almost all solder alloys is tin. Alloy elements such as lead, silver, copper, indi...
An Interveiw with Bob Bormann of Standard Printed Circuits
This year I had the pleasure of working with a circuit board company in Central New York called Standard Printed Circuits, Inc. From personal experien...
Dartmouth Student Asks Questions About SACm® Solder Alloy
Folks, Some years ago, a leading IC manufacturer decided that their R&D effort could benefit if analyzed for possible improvement – by hirin...
Bi/Sn/Ag: The Perfect Tabbing Ribbon Coating Solder Alloy?
Let’s quickly review the advantages of Bi/Sn/Ag alloy tabbing ribbon coating before we discuss them further: Low temperature melting point Pb-fr...
Is the PC Dead?
Folks, Let’s see how Patty is recovering from her conflict with Hal Lindsay……. Patty saw a link on one of the daily SMT Tech new...
Has Lead-Free RoHS Compliant Assembly Reliability and Cost "Arrived?"
Folks, I was at APEX 2013 San Diego this past week. San Diego is a great venue for the show, but I always forget how cold it can be (55-65°F...
Where is Tin Silver Solder, Now That You Need It?
Over the years, solder alloy choices have been pretty stable. In the last century, SN63 and SN62 could be found at any company making any k...
Choosing the Best Metallization for your NanoBond® Application
Since the NanoBond® process is almost instantaneous, fluxes are not used. (They just don’t have enough time to heat up to their activation t...
Preparing Surfaces for a NanoBond®
The first time I was taught how to solder (as a child), I was told: “All the surfaces need to be mechanically cleaned and chemically cleaned.&rd...